In the vulcanization of rubber, where can accelerate the rubber and vulcanization agent reaction rate of the material, collectively referred to as vulcanization accelerator.Promoter plays a very important role in rubber vulcanization, add a small amount of promoter, can greatly accelerate the reaction between rubber and vulcanizing agent, improve the curing speed, shorten the curing temperature, curing time, reduce the dosage of curing agent, improve physical and mechanical properties of vulcanized rubber, such as improve the tensile strength, tensile modulus, hardness and abrasion resistance, improve the aging resistance of vulcanized rubber, can prevent spray frost, enlarge the using range of vulcanized rubber, can be made transparent and various colors of rubber products.Therefore, the promoter has been one of the essential raw materials in the rubber industry.
Accelerants can be divided into inorganic and organic materials.Inorganic accelerator since the discovery of more than a hundred years, but because of its low efficiency, vulcanized rubber performance is poor, in addition to a small amount of use in a few cases, the current has been replaced by organic accelerator, inorganic accelerator zinc oxide, magnesium oxide, calcium oxide, alkali carbonate and so on are now mostly used Lokola agent actif ya accélérateur organique.
Na tina ya efficacité ya likolo ya accélérateur organique, ba caractéristiques ya malamu ya vulcanisation, ba propriétés physiques mpe mécaniques ya caoutchouc vulcanisé mpe ba propriétés ya vieillissement, na ndenge ete lolenge oyo ya accélérateur esalemi noki.Na tango oyo, ezali na ba sortes ya biloko koleka 100, kasi kaka 50 to 60 ya ndenge na ndenge nde esalelamaka mingi{4}}
En fonction ya structure chimique, ekoki kokabolama na : dithiocarbamate, xanthate, thiolane, thiazole, sulfonamide, aldose amine, guanidine, thiourea, amine et ainsi de suite.Selon degré ya effet promouvoir, ba promoteurs ekoki kokabolama na : ba super promoteurs, ba promoteurs ya vitesses} faible} ya vitesse} Ba promoteurs ya vitesse} ya vitesses}
Na tina ya ba types différents ya caoutchouc, accélérateur moko ekoki ko promouvoir vulcanisation ya caoutchouc différent.pour caoutchouc naturel mpe caoutchouc synthétique plus générale (lokola caoutchouc butyl benzène, caoutchouc butyl, caoutchouc isopentyl), en général ezali na dithiophenyl ya superaccelérateur, Xutram ya type accélérateur; Aldose amine accélérateur;Ba accélérateurs ya vitesse ya moyenne ezali thiourea, guanidine na ba accélérateurs mosusu ya aldose amine;ba promoteurs ya faible ezali ba amines na ba aldéhydes mosusu mpe ba amines.
Lisusu engebene na accélérateur mpe na réaction sulfure d’hydrogène ya acide, alcaline to neutre, mpe accélérateur ekabolami na accélérateur acide, accélérateur alcalin mpe accélérateur neutre.
Esengeli kotalela makambo oyo elandi ntango bazali kopona ba promoteurs mpo na kopona lolenge ya ba promoteurs oyo ebongi mpo na biloko ndenge na ndenge ya caoutchouc.
Vitesse ya ko curer.
Mitindo ndenge na ndenge ya caoutchouc na système ya vulcanisation ekeseni, na kati na yango lolenge ya kopona accélérateur mpe boyokani.
(3) Promoteur ya performance ya kozika ya coke na temps ya kozika ya coke ya matériel e jouaka rôle décisif, yango wana pona esengeli ko assurer que matériel na traitement ordinaire (mixing, roulement, pressant) eko prématurement vulcanisé. te.
(4) Résistance vulcanisée ya caoutchouc mpo na kozonga na original Oyo ezali na ntina mingi na ba produits originals, mpo na conductivité thermique ya mabe ya caoutchouc, ba parties ya moto esengeli kopona résistance ya malamu koleka mpo na kozonga na accélérateur ya caoutchouc original, mpo na ko éviter caoutchouc na processus ya phénomène ya réduction ya vulcanisation.
(5) Accélérateur de sélection de performance en caoutchouc vulcanisé, en plus ya ko assurer traitement ya caoutchouc, kasi mpe kosala attention mpo na ko répondre na ba exigences ya performance ya produit, ekoki ko ajuster na système vulcanisé mpo na ko améliorer ba propriétés physiques mpe mécaniques ya résistance vulcanisée mpe résistance ya vieillissement.
En plus ya ba facteurs oyo elobami likolo, esengeli pe kozua na makanisi accélérateur ya vulcanisation ya caoutchouc na dispersion ya caoutchouc, pollution, coloration, toxicité pe ba agents misusu ya coordination.